Interfacial crosslinked controlled thickness graphene oxide thin-films through dip-assisted layer-by-layer assembly means

Kandjou, Vepika, Hernaez Saenz De Zaitigui, Miguel ORCID: https://orcid.org/0000-0001-7878-4704, Acevedo Munoz, Beatriz and Melendi-Espina, Sonia ORCID: https://orcid.org/0000-0002-1083-3896 (2019) Interfacial crosslinked controlled thickness graphene oxide thin-films through dip-assisted layer-by-layer assembly means. Progress in Organic Coatings, 137.

Preview

PDF (Accepted_manuscript) - Accepted Version Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (1MB) | Preview

Abstract

The augmentation of research in graphene based thin films has been of great interest to various current industrial stakeholders. This is mainly due to the wide scope of films applications, ranging from nanoelectronics to separation membranes. Therefore, establishing a relation between graphene based thin film key characteristics and the fabrication operating conditions is of high significance. This study entails the successful fabrication of controlled-thickness crosslinked graphene oxide (GO) thin films on inexpensive silicon-based glass slide substrates. The method of film fabrication used is the dip-assisted layer-by-layer assembly, which has an added advantage of step-control of thin film thickness, good film uniformity and continuity. The thickness was primarily tuned through the use different sized crosslinkers; a covalent based sub-nanometer sized p-phenylenediamine and an electrostatic based polyethyleneimine on an interchangeable assembly with GO. Pre film fabrication, Fourier Transform Infra-Red and X-Ray Photoelectron Spectroscopy characterizations were carried out to determine the nature of interactions between GO and the crosslinkers. Post film fabrication, scanning electron microscopy, water contact angle measurements and profilometry analysis were undertaken for film continuity, hydrophilicity and thickness measurements respectively. A strong linear trend between film thickness of the differently crosslinked films and the number of bi-layers was established.

Item Type:	Article
Faculty \ School:	Faculty of Science > School of Engineering (former - to 2024)
UEA Research Groups:	Faculty of Science > Research Groups > Sustainable Energy Faculty of Science > Research Groups > Materials, Manufacturing & Process Modelling
Depositing User:	LivePure Connector
Date Deposited:	18 Sep 2019 10:30
Last Modified:	07 Nov 2024 12:41
URI:	https://ueaeprints.uea.ac.uk/id/eprint/72275
DOI:	10.1016/j.porgcoat.2019.105345

Downloads

Actions (login required)

View Item