Hydrothermal synthesis of reduced graphene oxide-LiNi0.5Mn1.5O4 composites as 5V cathode materials for Li-ion batteries

Mo, Mingyue, Chen, Hongyu, Hong, Xiaoting, Hui, K. S. ORCID: https://orcid.org/0000-0001-7089-7587, Ye, Chengcong and Lai, Ke (2017) Hydrothermal synthesis of reduced graphene oxide-LiNi0.5Mn1.5O4 composites as 5V cathode materials for Li-ion batteries. Journal of Materials Science, 52 (5). pp. 2858-2867. ISSN 0022-2461

[thumbnail of Accepted manuscript]
PDF (Accepted manuscript) - Accepted Version
Download (969kB) | Preview


Composite materials consisting of reduced graphene oxide and LiNi0.5Mn1.5O4 were in situ prepared by a simple one-step hydrothermal treating method. The physical property and electrochemical performance of the composite materials were characterized by X-ray diffraction, Raman spectroscopy, scanning electron microscopy, X-ray photoelectron spectroscopy, cyclic voltammetry, charge/discharge testing, and electrochemical impedance spectroscopy. The results demonstrate that the graphene oxide is partially reduced and uniformly in situ anchored on the surface of LiNi0.5Mn1.5O4. As a result, the specific surface area of the composite material dramatically increases from 0.2488 to 8.71 m2 g−1, and the initial specific discharge capacity improves from 125.8 to 140.2 mAh g−1, respectively. Furthermore, the capacity retention maintains 95.8% after 100 cycles, and the electrode polarization has significantly been lessened. At rates of 1, 2, and 5 C, the composite material with 5% reduced graphene oxide can deliver much higher capacities than the pristine LiNi0.5Mn1.5O4. Moreover, AC impedance test results show that the interfacial charge transfer impedance obviously reduced. It is confirmed that the introduction of reduced graphene oxide through hydrothermal treating is effective to enhance the electrochemical performance of the composite material.

Item Type: Article
Faculty \ School:
Faculty of Science > School of Engineering
UEA Research Groups: Faculty of Science > Research Groups > Energy Materials Laboratory
Related URLs:
Depositing User: Pure Connector
Date Deposited: 21 Dec 2016 00:02
Last Modified: 13 Apr 2023 13:51
URI: https://ueaeprints.uea.ac.uk/id/eprint/61798
DOI: 10.1007/s10853-016-0579-z


Downloads per month over past year

Actions (login required)

View Item View Item