Synthesis of high surface area phosphosilicate glasses by a modified sol-gel method

Aronne, Antonio, Turco, Maria, Bagnasco, Giovanni, Pernice, Pasquale, Di Serio, Martino, Clayden, Nigel J., Marenna, Elisa and Fanelli, Esther (2005) Synthesis of high surface area phosphosilicate glasses by a modified sol-gel method. Chemistry of Materials, 17 (8). pp. 2081-2090. ISSN 0897-4756

Full text not available from this repository. (Request a copy)

Abstract

High surface area phosphosilicate glasses were synthesized by a new sol-gel method and characterized for structural, textural, and acid properties by X-ray diffraction, thermogravimetry/differential thermal analysis, IR spectroscopy (Fourier transform and diffuse reflectance Fourier transform), solid state P-31 and Si-29 NMR spectroscopy, N-2 adsorption, and NH3 temperature programmed desorption. The glasses were synthesized by a sol-gel route hydrolyzing the precursors in an almost solely aqueous environment. Microstructural changes occurring during the conversion of the gels into the corresponding glasses were investigated. For all dried gels (383 K), the elimination of organic residues was complete at 673 K. After this heat treatment, ca. 80% of the phosphorus was present as free phosphoric acid except for the sample with the highest P content for which the percentage dropped to ca. 47%. Textural properties of samples treated at 673 K were greatly influenced by the composition. Surface area decreased and pore dimension increased with increasing phosphorus content, indicating a gradual transformation of the siloxane matrix from microporous to mesoporous. Br phi nsted acid sites of differing strength, mainly related to the presence of phosphoric acids, were found. The surface concentration and strength of acid sites increased with phosphorus content.

Item Type: Article
Faculty \ School: Faculty of Science > School of Chemistry
UEA Research Groups: Faculty of Science > Research Groups > Physical and Analytical Chemistry (former - to 2017)
Depositing User: Rachel Smith
Date Deposited: 14 Jun 2011 14:37
Last Modified: 24 Oct 2022 02:13
URI: https://ueaeprints.uea.ac.uk/id/eprint/32504
DOI: 10.1021/cm047768t

Actions (login required)

View Item View Item